Don't sacrifice toughness for wear resistance: Stellite 6B offers both. An extensive hot forging process transforms brittle ingot into the tough, wear-resistant Stellite 6B that meets aerospace material specification AMS
For wrought grades Stellite™ 6B and Stellite™ 6K, the wrought or hot forging method of production leads to improvements of the resulting material with regards to: Stellite™ 6B is stocked in standard mill
AMS 5894, Cobalt 6B, Stellite®6B, UNS R30016 | 스틸맥스
2017225 · AMS 5894 는 UNS R30016 , Stellite 6B, 또는 Cobalt Alloy 6B Bar (봉강)와 Sheet and Plate (판)에 대한 규정이고. Sheet and Plate (판)의 경우는 두께 1inch (25mmt) 까지. Round Bars 인 경우는 3-1/2 inch (89mm) 까지입니다. AMS A5894 Standard Specification : Cobalt Alloy, Bars, Sheets, and Plate. 60Co-28Cr-4.5W-1.15C ...
Stellite® 6 Material Information | Hardface Welding and
Stellite ® 6 is a Cobalt based alloy composed of 27%-32% chrome, 4%-6% Tungsten, 1%-2% Carbon, 3%-4% Nickel, 1%-2% Silicon and 3%-4% Iron. Due to the alloying, Stellite ® 6 has a matrix consisting of complex carbides that are especially useful for applications requiring excellent hardness and wear resistance. Its hardness values range between 36
For wrought grades Stellite™ 6B and Stellite™ 6K, the wrought or hot forging method of production leads to improvements of the resulting material with regards to: Stellite™ 6B is stocked in standard mill forms of flat
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C; Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate; Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816°C
Material Stellite 6 : Machinig Data Sheet (Machining Doctor)
Machining Material Stellite 6. Stellite 6 is a Cobalt-based heat resistant superalloy ( HRSA) material with a Machinability rating of 19% and Hardness of 32 HRC. Stellite 6 has 66% cobalt, 3% nickel and additional alloying elements per the below table. Cobalt-based alloys excel in wear resistance and chemical stability in harsh and hot conditions.
Stellite – Density – Strength – Hardness – Melting Point
2023314 · Melting point of Stellite is 1297 °C. Note that, these points are associated with the standard atmospheric pressure. In general, melting is a phase change of a substance from the solid to the liquid phase. The melting point of a substance is the temperature at which this phase change occurs. The melting point also defines a
2023312 · Stellite®6 은, Cobalt-Chromium (Co-Cr) 합금으로 Deloro Stellite 회사의 Trademark. Rod,Castings, AMS 5387, UNS No R30006, Bar/Plate/Sheet인 AMS 5894, UNS No R30016 Stellite®6, Cobalt Super Alloy, Kennametal Trademark STEELMAX Metal Story